| Primary information |
|---|
| SAPdb_ID | 1443 |
| PMID | 24085660 |
| Year | 2013 |
| Name | Fmoc-LL |
| Sequence | LL |
| N-Terminal Modification | Fmoc(fluorenylmethoxycarbonyl) |
| C-Terminal Modification | Free |
| Non-terminal Modication | None |
| Length | 2 |
| Peptide/Conjugate/Mixture | Peptide |
| Conjugate Partner | NA |
| Technique | TEM (Transmission Electron Microscopy) and WAXS(Wide Angle X - Ray scattering) |
| Solvent | Water + 0.1M Hcl + 0.5 M NaOH |
| Method | Fmoc-dipeptide was suspended in water. Sodium hydroxide (0.5 M) was gradually added to the aqueous suspensions of Fmoc-dipeptide until pH 10.5 was reached. The samples were vortexed and sonicated for one minute to fully dissolve the peptide amphiphiles. To obtain required pH, a required volume of dilute hydrochloric acid (0.085 M) was then added dropwise to the solution. Solution sonicated and vortexed. Next, the samples were heated to 75–80 ◦C until fully dissolved and homogenised. The samples were subsequently cooled and maintained at 4 ◦C for ∼ 12 hours (overnight) to promote gelation. |
| Concentration | 10mmol/L |
| pH | pH 4.3 - 6.8 |
Temperature
| 4 °C |
| Incubation Period | ~ 12 hours |
| Self-Assembly Formation | Yes |
| Type of Self-Assembly | Nanofibers |
| Size of Self-Assembled structure | NA |
| Linear/Cyclic | Linear |
| Stability of Nanostructure | NA |
| Comment | NA |